Aluminium 2014 square bars are tough, precision-crafted metal products that find their way into a variety of fields, including aerospace, automotive, and industrial sectors. Made from the 2014 aluminium alloy, these bars boast impressive mechanical strength, decent wear resistance, and moderate corrosion resistance. Their square shape not only makes them easy to handle but also versatile for machining, structural work, and fabrication tasks. With a range of sizes, lengths, and tempers available, Aluminium 2014 square bars are produced to meet stringent industry standards, ensuring they deliver reliable performance, precise dimensions, and long-lasting durability even in challenging environments.
Aluminium 2014 is an aluminium-copper alloy with approximately 3.9-5.0% copper content and smaller amounts of manganese, iron, silicon, and zinc. This composition imparts excellent mechanical properties, including high strength, good machinability, and superior fatigue resistance. The alloy’s tensile strength ranges from 310 to 430 MPa, yielding between 260 to 320 MPa. The hardness is typically around 95 to 105 Brinell. Aluminium 2014’s high strength, machinability, and good thermal conductivity make it ideal for aerospace applications, structural components, and high-stress engineering uses.
Specification : ASTM B 221 ASME SB 221, B211, B565, B316 1100, AMS 4102
Standard : ASTM, BS and all International Standards
Temper : O, H12, H14, H16, H18, H22, H24, H26, H32, H112
Length : 100 mm To 3000 mm Long & Above
Size : 5 mm To 500 mm
| Aluminium 2014 | Fe | Si | Mg | Mn | Cu | Zn | Ti | Al |
| 0.7 | 0.50 – 1.20 | 0.2 – 0.8 | 0.4 – 1.2 | 3.9 – 5.0 | 0.25 | 0.15 | 93.5 |
| Material | Temper | Diameter (mm) | Tensile Strength min ((N/mm²) | Yield Strength (min) (N/mm²) | Elongation on 5.65 V (min) |
| 2014 Bar | T4 | <20 | 370 | 230 | 11 |
| 2014 Bar | T4 | 20-75 | 390 | 250 | 11 |
| 2014 Bar | T4 | 75-150 | 390 | 250 | 9 |
| 2014 Bar | T4 | 150-200 | 370 | 230 | 8 |
| 2014 Bar | T6510 | 20-75 | 480 | 435 | 7 |
| 2014 Bar | T6510 | 75-150 | 465 | 420 | 7 |
| 2014 Bar | T6510 | 150-200 | 435 | 390 | 7 |
Density : 2.8 g/cm3
Melting point : 510°C (950°F)
Tensile Strength : 414 MPa – 60000 psi
| STANDARD | UNS | WERKSTOFF NR. | European Standard | BS (OLD) | ISO | USA (AA) | GERMANY (DIN) | IS | Canadian |
| Aluminium 2014 | A92014 | 3.1255 | EN AW-2014 | HE15 | AlCu4SiMg | 2014 | AlCuSiMn | 24345 | B26S |
These square bars are crafted from 2014 aluminium alloy, which mainly consists of aluminium with copper as the primary alloying element, along with trace amounts of magnesium, manganese, and silicon. This unique blend gives them high tensile strength, outstanding fatigue resistance, and solid hardness. On the mechanical side, they show moderate resistance to corrosion, high wear resistance, and excellent machinability. Their sturdy design allows them to handle heavy mechanical loads, making Aluminium 2014 square bars perfect for aerospace components, automotive parts, and precision engineering tasks.
Yes, we offer custom sizes for Aluminum 2014 Square Bars to meet specific project needs. Our team at Himansh Aluminium is committed to providing customized solutions for all your requirements. For more details, contact us at sales@himanshaluminium.com
You’ll find Aluminium 2014 square bars in a variety of applications, from aircraft fittings and automotive chassis components to industrial machinery and structural frameworks. They’re also used in gears, shafts, and heavy-duty fabrication projects that demand strength and durability. Thanks to their lightweight nature, exceptional mechanical strength, and fatigue resistance, Aluminium 2014 square bars are a go-to choice for industries that need high-performance, dependable, and long-lasting aluminium solutions.